Excellent processing and mechanical properties
High mechanical properties, suitable for high tension system
Good dispersion, suitable forlow tension system
Direct Rovings for LFT are coated with a silane-based sizing and compatible with PP, PA, TPU and PET resins.
LFT-D
Polymer pellets and glass roving are all introduced into a twin-screw extruder where the polymer is melted and compound is formed.
Then the molten compound is directly molded into the final parts by injection or compression molding process.
LFT-G
The thermoplastic polymer is heated to a molten phase and pumped into the die-head . The continuous roving is pulled through a dispersion die to ensure the glass fiber and polymer impregrated fully and to get consolidated rods. After cooling, the rod is chopped into reinforced pellets.
Product Code | Filament Diameter(μm) | Standard Linear Density (Tex) | Moisture (%) | Breaking Strength (N/tex) | Resin Compatibility | Typical Applications | |||
PPTH | 14-17 | 2000/2400/4800 | ≤0.1 | ≥0.25 | PP, PA,TPU, PET | (Automobile/Truck/Building materials/Electronics/Infrastructure) | |||
E glass fiber direclty roving | ISO1888 | ISO1889 | ISO3344 | ISO3341 |